Zheflon®FL2009 PVDF - Water treatment membrane grade
It has good solubility in NMP, DMAc, suitable for dry NIPS process, and has wide applications in water treatment industry.
| Categories | PVDF Extrusion Grade |
|---|---|
| Brand | Zheflon PVDF & Flurine FKM Manufacturer |
| Model | FL2009 |
| Water Absorption（%） | ≤0.15 |
| Melt Flow Rate（g/10min） | 2.0-8.0 |
| Secondary Melting Point（℃） | 165-175 |
| Break Strength/mPa | ≥25 |
| Update Time | Apr 25,2025 |
Detail Information
Description
Zheflon FL2009 is a powdery polyvinylidene fuoride (PVDF) resin produced through a suspension polymerization process. It has excellent acid and alkali resistance, as well we good mechanical strength and toughness. It has good solubility in NMP, DMAc, and it's suitable for dry TIPS process, making it widely applicable in the water treatment industry.
Technical Specifications
Specifications | Range | Reference Standard | ||||
Appearance | White powder | / | ||||
Moisture Content(%) | ≤0.10 | GB/T6284 | ||||
Rotational Viscosity (mPa.s) | 50-250 | 1gPVDF:9g DMAc,#2spindle,30°C,GB/T 10247 | ||||
Molecular Weight(Da) | 750,000-800,000 | GB/T 21864 | ||||
Secondary Melting Point (℃） | 165-175 | GB/T 19466 | ||||
Melt Flow Rate（g/10min） | 1-10 | Load 5kg, 230℃, GB/T 3682 | ||||
Contact Immediately
We have a dedicated team of technical experts ready to assist you with your most challenging projects. Discover cost-effective customized solutions for exceptional performance and value. Contact us today – we are eager to take on the challenge!
- Name
- Tel
- *Title
- *Content
Products
Related Products
Let's Innovate Together
We have a dedicated team of technical experts ready to help you with your most challenging projects, so contact us today - we're ready for the challenge!
Founded 2007, is a tech enterprise specializing in fluorine-based materials. We drive renewable energy and sustainability through innovation.